Inoue, Takehiro
Effect of Stress Reflection on Dynamic Stress Intensity Factor in Crack Arrest Toughness Testing
Handa, Tsunehisa (Steel Research Laboratory, JFE Steel Corporation) | Tagawa, Tetsuya (Steel Research Laboratory, JFE Steel Corporation) | Shimada, Yusuke (Nippon Steel and Sumitomo Metal Corporation) | Kawabata, Tomoya (University of Tokyo) | Inoue, Takehiro (Nippon Steel and Sumitomo Metal Corporation) | Kaneko, Masahito (Kobe Steel, Ltd.) | Sugimoto, Kei (ClassNK) | Aihara, Shuji (University of Tokyo) | Shibanuma, Kazuki (University of Tokyo)
Brittle Crack Arrest Toughness for Extremely Thick Steel Plates -Required Kca Value of Steel Plates With Thickness of 100 Mm Used in Ultra-Large Container Ships-
Matsumoto, Kazuyuki (Nippon Kaiji Kyokai) | Fukui, Tsutomu (Nippon Kaiji Kyokai) | Nanno, Shota (Nippon Kaiji Kyokai) | Aihar, Shuji (University of Tokyo) | Kawabata, Tomoya (University of Tokyo) | Shibanuma, Kazuki (University of Tokyo) | Inoue, Takehiro (Material Properties Evaluation Divsion) | Okawa, Teppei (Steel Research Laboratory) | Tagawa, Tetsuya (Steel Research Laboratory) | Tajika, Hisakazu (Steel Research Laboratory) | Imamura, Hiroki (Plate & Products Marketing & Technical Service Department)
Investigation of Isothermal Crack Arrest Test Procedure Consistent With Kca - Development of Isothermal Crack Arrest Test Procedure – 2
Tagawa, Tetsuya (JFE Steel Corporation) | Inoue, Takehiro (Nippon Steel & Sumitomo Metal Corporation) | Tajika, Hisakazu (JFE Steel Corporation) | Okawa, Teppei (Nippon Steel & Sumitomo Metal Corporation) | Imamura, Hiroki (KOBE STEEL, LTD.) | Kawabata, Tomoya (University of Tokyo) | Shibanuma, Kazuki (University of Tokyo) | Aihara, Shuji (University of Tokyo)
Effects of Test Parameters on Crack Arrest Temperature in Isothermal Brittle Crack Arrest Test -Development of Isothermal Crack Arrest Test Procedure −1
Inoue, Takehiro (Nippon Steel and Sumikin Technology Co. Ltd.) | Tagawa, Tetsuya (JFE Steel Corporation) | Okawa, Teppei (Nippon Steel and Sumitomo Metal Corporation) | Tajika, Hisakazu (JFE Steel Corporation) | Imamura, Hiroki (KOBE STEEL, LTD.) | Matsumoto, Kazuyuki (Nippon Kaiji Kyokai) | Fukui, Tsutomu (Nippon Kaiji Kyokai) | Nanno, Shota (Nippon Kaiji Kyokai) | Kawabata, Tomoya (The University of Tokyo) | Shibanuma, Kazuki (The University of Tokyo) | Aihara, Shuji (The University of Tokyo)
Simplified Evaluation of Brittle Crack Arrest Toughness in Heavy-Thick Plate by Combined Small-Scale Tests
Okawa, Teppei (Nippon Steel & Sumitomo Metal Corporation) | Shirahata, Hiroyuki (Nippon Steel & Sumitomo Metal Corporation) | Nakashima, Kiyotaka (Nippon Steel & Sumitomo Metal Corporation) | Yanagita, Kazuhisa (Nippon Steel & Sumitomo Metal Corporation) | Inoue, Takehiro (Nippon Steel & Sumitomo Metal Corporation)
Cryogenic leakage risk analysis for FLNG and use of brittle crack arresting material as a risk mitigation measure
Usami, Akio (Nippon Kaiji Kyokai (ClassNK)) | Kishimoto, Naohiko (JGC Corporation) | Kusumoto, Hiroki (Japan Marine United Corporation) | Kaneko, Fujio (National Maritime Research Institute) | Inoue, Takehiro (Nippon Steel & Sumitomo Metal Corporation)
Simplified Evaluation of Brittle Brack Arrest Toughness in Heavy-Thick Plate by Combined Small-scale Tests
Okawa, Teppei (Nippon Steel & Sumitomo Metal Corporation) | Shirahata, Hiroyuki (Nippon Steel & Sumitomo Metal Corporation) | Nakashima, Kiyotaka (Nippon Steel & Sumitomo Metal Corporation) | Yanagita, Kazuhisa (Nippon Steel & Sumitomo Metal Corporation) | Inoue, Takehiro (Nippon Steel & Sumitomo Metal Corporation)
Proposal of Test Method for Brittle Crack Arrest Toughness, Kca - Study on Standard Test Method for Crack Arrest Toughness, Kca -1-
Shimada, Yusuke (Nippon Steel and Sumitomo Metal Corp.) | Inoue, Takehiro (Nippon Steel and Sumitomo Metal Corp.) | Kawabata, Tomoya (Nippon Steel and Sumitomo Metal Corp.) | Handa, Tsunehisa (JFE Steel Corporation ) | Kaneko, Masahito (Kobe Steel, LTD) | Sugimoto, Kei (Nippon Kaiji Kyokai) | Aihara, Shuji (Tokyo University) | Shibanuma, Kazuki (Tokyo University)
Effect of Specimen Size and Applied Stress on Brittle Crack Arrest Toughness - Study on Standard Test Method for Crack Arrest Toughness, Kca -2 -
Shimada, Yusuke (Nippon Steel and Sumitomo Metal Corp.) | Inoue, Takehiro (Nippon Steel and Sumitomo Metal Corp.) | Kawabata, Tomoya (Nippon Steel and Sumitomo Metal Corp.) | Handa, Tsunehisa (JFE Steel Corporation ) | Kaneko, Masahito (Kobe Steel, LTD) | Sugimoto, Kei (Nippon Kaiji Kyokai) | Aihara, Shuji (The University of Tokyo) | Shibanuma, Kazuki (The University of Tokyo)